Characterizing the microstructures of mammalian enamel by synchrotron phase contrast microCT

The enamel of mammalian teeth is a highly mineralized tissue that must endure a lifetime of cyclic contact and is inspiring the development of next-generation engineering materials. Attempts to implement enamel-inspired structures in synthetic materials have had limited success, largely due to the absence of a detailed understanding of its microstructure. The present work used synchrotron phase-contrast microCT imaging to evaluate the three-dimensional microstructure of enamel from four mammals including Lion, Gray Wolf, Snow Leopard, and Black Bear. Quantitative results of image analysis revealed that the decussation pattern of enamel consists of discrete diazone (D) and parazone (P) bands of rods organized with stacking arrangement of D+/P/D-/P in all mammals evaluated; the D+ and D- refer to distinct diazone bands with juxtaposed rod orientations from the reference plane. Furthermore, the rod orientations in the bands can be described in terms of two principal angles, defined here as the pitch and yaw. While the pitch angle increases from the outer enamel to a maximum (up to ≈ 40°) near the dentin enamel junction, minimal spatial variations are observed in yaw across the enamel thickness. There are clear differences in the decussation parameters of enamel across species that are interpreted here with respect to the structural demands placed on their teeth. The rod pitch and band width of enamel are identified as important design parameters and appear to be correlated with the bite force quotient of the four mammals evaluated. Statement of significance: The multi-functionality of tooth enamel requires both hardness and resistance to fracture, properties that are generally mutually exclusive. Ubiquitous to all mammalian teeth, the enamel is expected to have undergone adaptations in microstructure to accommodate the differences in diet, body size and bite force across animals. For the first time, we compare the complex three-dimensional microstructure of enamel from teeth of multiple mammalian species using synchrotron micro-computed tomography. The findings provide new understanding of the “design” of mammalian enamel microstructures, as well as how specific parameters associated with the decussation of rods appear to be engineered to modulate its fracture resistance.