Zirconium aluminum carbides: New precursors for synthesizing ZrO ₂-Al₂O₃ composites

ZrO₂-Al₂O₃ nanocrystalline powders have been synthesized by oxidizing ternary Zr₂Al₃C₄ powders. The simultaneous oxidation of Al and Zr in Zr₂Al ₃C₄ results in homogeneous mixture of ZrO₂ and Al₂O₃ at nanoscale. Bulk nano- and submicro-composites were prepared by hot-pressing as-oxidized powders at 1100°-1500°C. The composition and microstructure evolution during sintering was investigated by XRD, Raman spectroscopy, SEM, and TEM. The crystallite size of ZrO₂ in the composites increased from 7.5 nm for as-oxidized powders to about 0.5 μm at 1500°C, while the tetragonal polymorph gradually converted to monolithic one with increasing crystallite size. The Al₂O₃ in the composites transformed from an amorphous phase in as oxidized powders to θ phase at 1100°C and α phase at higher temperatures. The hardness of the composite increased from 2.0 GPa at 1100°C to 13.5 GPa at 1400°C due to the increase of density.