Synthesis and characterization of super occluded LiCl-KCl in zeolite-4A as a chloride salt waste form intermediate

This paper reports the hygroscopic properties of eutectic LiCl-KCl after absorption into zeolite-4A, up to salt loadings of 75 wt%. Samples of the salt occluded zeolite were hydrated in a humidity chamber at constant temperature and relative humidity for up to 100 h. At up to 45 wt% salt loading, the un-occluded phase of salt consisted primarily of NaCl, which forms when the Na⁺ ions present in the zeolite framework exchange with Li⁺ and K⁺ ions from the eutectic LiCl-KCl. This results in minimal water absorption and corrosion of contacted stainless steel. At greater than 45 wt% salt loading, water absorption and corrosion progressively worsened. The mixture has a significant amount of excess LiCl-KCl, making it highly hygroscopic. This study reveals an option for the intermediate treatment of waste salt from spent nuclear fuel electrorefiners that could facilitate it to be stored in a non-inert atmosphere for extended periods of time before final conversion into a permanent waste form.