Microstructure study of U-35 wt.% Zr alloy after quick annealing at 650 °c

Uranium-35 wt.% zirconium (U-35 wt.% Zr) alloy was annealed for 1 h and 24 h at 650 °C and characterized to understand the early-stage microstructure evolution. Dendritic microstructure with fine (∼300 nm in length) α-U precipitates clustered between dendrite branches were observed in the 1-h annealed sample. After 24-h annealing at 650 °C, the α-U precipitates coarsened, and the dendritic microstructure disappeared because of microstructure homogenization. Furthermore, microchemical homogenization observed with energy-dispersive X-ray spectroscopy analysis suggests that α-U precipitates are approaching thermodynamic equilibrium in the 24-h annealed sample. The findings from this study have potential impacts on the manufacturing and computer modeling of metallic nuclear fuel.