Micropillar Compression of Additively Manufactured 316L Stainless Steels after 2 MeV Proton Irradiation: A Comparison Study between Planar and Cross-Sectional Micropillars

A micropillar compression study with two different techniques was performed on proton-irradiated additively manufactured (AM) 316L stainless steels. The sample was irradiated at 360 °C using 2 MeV protons to 1.8 average displacement per atom (dpa) in the near-surface region. A comparison study with mechanical test and microstructure characterization was made between planar and cross-sectional pillars prepared from the irradiated surface. While a 2 MeV proton irradiation creates a relatively flat damage zone up to 12 µm, the dpa gradient by a factor of 2 leads to significant dpa uncertainty along the pillar height direction for the conventional planar technique. Cross-sectional pillars can significantly reduce such dpa uncertainty. From one single sample, three cross-sectional pillars were able to show dpa-dependent hardening. Furthermore, post-compression transmission electron microscopy allows the determination of the deformation mechanism of individual micropillars. Cross-sectional micropillar compression can be used to study radiation-induced mechanical property changes with better resolution and less data fluctuation.