Linking microstructure to creep behavior in vertically and horizontally built LPBF Haynes 282 compared with wrought material via θ-projection

Laser Powder Bed Fusion (LPBF) has emerged as a promising route for fabricating intricate geometries in high-performance alloys. Haynes 282 (H282) is a strong candidate for applications such as heat exchangers or engines due to its excellent creep strength and thermal stability; however, the long-term creep behavior of LPBF-processed H282 remains poorly understood. In this study, the θ-projection method is used to analyze and extrapolate the creep behavior of vertically built LPBF, horizontally built LPBF, compared to wrought H282 tested at 816 °C. Vertically built LPBF H282 exhibits the lowest minimum creep rate (MCR), while the horizontally built condition shows a higher MCR comparable to that of wrought H282. Despite these differences, both LPBF conditions exhibit significantly shorter rupture life and reduced rupture strain than the wrought material, with the most severe degradation observed in the horizontal builds, consistent with an earlier onset of tertiary creep and accelerated strain-rate evolution. Microstructural characterization reveals that both LPBF and wrought H282 exhibit abundant twin-related boundary character; however, their grain boundary topologies differ markedly. The wrought alloy contains a higher fraction of low-angle grain boundaries and continuous twin lamellae, whereas the LPBF microstructure is characterized by a suppressed low-angle boundary population and fragmented twin-related boundaries embedded within irregular high-angle grain boundary networks. Fractographic analysis further reveals predominantly intergranular cracking in LPBF H282, accompanied by grain-boundary-decorated carbides, Al₂O₃ inclusions, and high-aspect-ratio pores. These results demonstrate that grain boundary topology, rather than minimum creep rate alone, plays a critical role in governing creep damage accumulation and rupture behavior in LPBF and wrought H282.