Imaging and Analysis of Insoluble Electrorefiner Material

Throughout pyroprocessing efforts at the Hot Fuel Examination Facility (HFEF), insoluble material has accumulated in the Electrorefiner (ER) vessel. The objective of this effort was to analyze the accumulated material to determine its origin. Material was removed from the ER salt bath and distilled to remove excess salt prior to performing analysis. Three samples were sent for chemical and isotopic analysis and underwent an ethyl acetate-bromine dissolution to segregate the oxide fraction from the metal fraction. Actinide concentrations were determined using a quadrupole–inductively coupled plasma–mass spectrometer (Q-ICP-MS). Three additional samples were sent for morphologic and elemental analysis by scanning electron microscopy (SEM) with Energy Dispersive X-ray (EDX) analysis at the Irradiated Materials Characterization Laboratory (IMCL). Analyses suggest that the material is primarily composed of UO2. with a small fraction of metal. This study draws no single conclusion as to the origin of the insoluble material in the ER. The particle sizes and morphologies observed in SEM micrographs indicate that the larger particles observed may be a result of introducing material to the ER that has not been completely reduced in Oxide Reduction (OR) operations, which precede electrorefining. Smaller particles may be due to reactions with oxygen and moisture present in HFEF. This research suggests that microscopic analysis of fuel particles before and after OR operations (including after distillation) as well as the uranium product collected on the cathode in the ER would increase understanding about particle morphology within the pyrochemical process.