Directed energy deposition of Haynes 282 nickel superalloy

Laser powder directed energy deposition was employed to fabricate Haynes® 282 Ni-based superalloy for high temperature creep testing. Material was heat treated using a single-step aging heat treatment of 800 °C for 4 h. Microstructural analysis was conducted in the as-deposited, solution-annealed, and age-hardened conditions. γ′ precipitates were absent in the as-deposited and annealed condition but formed during aging with an average size of 48.5 ± 12 nm. γ’ denuded zones ranging in thickness from 73 to 469 nm were observed adjacent to an effectively continuous grain boundary carbide film that covered 72.5% of the measured boundary length. The heat-treated material contained a high-volume fraction of TiC carbides ranging in size from 38 to 457 nm. Electron backscatter diffraction showed partial recrystallization, with 77-83% recrystallized area and a heterogeneous grain-size distribution. Creep testing at 750 °C at 300, 320, and 350 MPa revealed significantly inferior performance compared to wrought material, with higher strain rates, earlier tertiary onset, and shorter rupture lives. Fractography shows that failure was dominated by intergranular rupture. Post rupture microstructural analysis results suggest that the creep behavior was primarily governed by the non-equilibrium interface network rather than the bulk γ/γ’ matrix. The findings indicate that achieving wrought-like creep performance necessitates substantial improvements in the additive process, specifically focusing on enhanced homogenization, full recrystallization, and precise control over the morphology and distribution of carbides.