Development of Graphite Thermal and Mechanical Modeling Capabilities in Grizzly

Nuclear-grade graphites are used extensively in the core designs of multiple types of advanced nuclear reactors. In the reactor environment, graphite is exposed over long durations to extreme conditions, including high temperatures, radiation and potentially molten salt and oxygen. Exposure to these conditions can cause several degradation mechanisms in graphite, including nonuniform volumetric strains induced by irradiation and thermal expansion, which lead to stresses that can compromise the performance of graphite components. Evaluating component integrity, predicting component performance over the reactor lifetime, and developing design standards all require robust tools for predicting fracture initiation and propagation in graphite structural components in nuclear reactors. This report documents progress in an ongoing effort to develop modeling and simulation tools in the Grizzly code for predicting the performance of graphite exposed to reactor conditions. Recent developments include a set of thermal and mechanical models that now include the IG-110, NBG-18, and H-451 graphite grades. Improvements have also been made to a nonlinear damaged plasticity model applicable to predicting damage under tension and compression to quasibrittle materials, including graphite. In addition, enhancements have been made to the extended finite element method implementation targeted at simulating graphite fracture. These include new capabilities for crack nucleation in the interior of a solid body, improved treatment of crack nucleation on free surfaces, and more robust modeling approaches for crack growth approaching free surfaces or other cracks.