Chemical Interaction of Palladium in Uranium Oxycarbide Nuclear Fuel Kernel

Tri-structural Isotropic (TRISO) particle fuel is the preferred choice for the newest and next-generation high-temperature nuclear reactors due to its robust construction [1]. The fuel design effectively contains fission products inside the particle at extremely high temperatures [2]. However, the effect of transition metal fission products on fuel performance and structural integrity remains largely unknown, creating uncertainties in predicting fuel performance and potential failure mechanisms [2]. For example, palladium (Pd) has a strong tendency to form intermetallic phases with uranium (U). These new phases tend to be hard and brittle which could lead to fracture of fuel kernel during irradiation [3,4]. Pd is not normally produced in high concentrations in normal fission reactions however, driving the production of Pd into the locality of a Uranium Oxycarbide (UCO) nuclear fuel provides an opportunity to closely observe the diffusion and chemical interactions. This study focuses on detailed transmission electron microscopy characterization of the intermetallic phases formed by the interaction between a UCO kernel and a Pd bar after annealing at 1100 °C for 100 hours.

Figure 1 provides an overview of the UCO kernel in contact with the Pd bar. The UCO-Pd sample surface was examined using a Focused Ion Beam (FIB) Quanta 3D FEG FEI in VCD detector mode at 10kV, 83pA to reveal surface features. Several key surface features in the interaction region were observed including: (1) a small area with dendritic microstructure, (2) color contrast near the UCO kernel and Pd boundary, and (3) darker and lighter regions throughout the sample surface.

To analyze diffusion behavior, FIB was used to prepare lamellae from five different areas of the UCO-Pd sample, as well as one for the as-received sample. These lamellae were examined using a Scanning Transmission Electron Microscope ThermoFisher Spectra 300 (STEM-Spectra). Energy Dispersive Spectroscopy results confirmed the diffusion between the UCO fuel and Pd bar. Figure 2 shows the identified phases of UC, UO2, and Pd dispersed throughout the interaction region. It was also found that the Pd concentration decreases as the radial distance from the UCO-Pd interface increases. The Pd concentration was 36.93% atomic fraction 11µm from the interaction region then decreased to 7.51% atomic fraction at 257 µm away from the interaction region. Figure 3 shows how concentrations of U and Pd vary across the interaction zone, highlighting the extent of diffusion.

This study confirms that Pd interacts with surrounding material to form U-Pd phase and diffusion zones. These diffusion zones vary in composition depending on its radial distance from the point of contact with the Pd bar. These findings contribute to a deeper understanding of the fission product behavior in high temperature nuclear fuels, aiding in the prediction and mitigation of potential fuel degradation mechanisms.